CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels

I'm Online Chat Now

CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels

CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels
CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels

Large Image :  CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels

Product Details:
Place of Origin: Dongguan, China
Brand Name: Tasuns
Certification: CE, SGS, ISO
Model Number: PMI Foam
Payment & Shipping Terms:
Minimum Order Quantity: 0.5cbm
Price: Negotiable
Packaging Details: Plywood
Delivery Time: 7-10 days for sample
Payment Terms: T/T, L/C
Supply Ability: 100cbm/week

CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels

Description
Deflection: 19mm Bending Strength: 5.5Mpa
Flexural Modulus: 195Mpa Closed Cell Rate: 98%
Tensile Modulus: 200Mpa Tensile Strength: 3.9Mpa
Elongation At Break: 2.7Mpa Shear Strength: 2Mpa
Shear Modulus: 63Mpa Origin: China
High Light:

CNC Machined pmi core

,

19mm foam sandwich panels

,

5.5Mpa pmi core

CNC Machined PMI Core For Medical Equipment

 

Why use PMI foam for x-ray medial board?

       PMI stands for polymethacrylimide. PMI foam cores are one of the strongest options for building Sandwich composite panels. For the same density, PMI foam cores offer some of the highest overall strengths and stiffnesses of foam cores. PMI foam cores have mainly been used in higher performance composite parts such as helicopter rotor blades, ailerons and stringer profiles in pressure bulkheads, high speed trains, UAVs, medical equipments, radome and antennas.

 

CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels 0

 

Tasuns PMI foam specification: 

  1) fine pores

  2) coarse pores

  3) ultra-fine pores.

Density
(kg/m³)
Model Mechanical properties at room temperature
Compressive strength Compression modulus Tensile Strength Tensile modulus Elongation at break Shear strength Shear modulus Bending strength Flexural modulus Deflection Closed cell rate
Mpa Mpa Mpa Mpa % Mpa Mpa Mpa Mpa mm %
Testing standard GB/T 8813-2008 GB/T 9641-1988 GB/T 1455-2008 GB/T 8812.2-2007 GB/T 10799-2008
32 XK32 0.32 14 0.66 28 3.8 0.28 7.6 0.86 31 22 99
CX30 0.42 20 0.56 39 0.69 1 31 30
40 CK40 0.6 34 0.9 54 1.7 0.4 19 1.3 55 15
CX40 0.72 29 1.2 51 3.4 1.7 58 33
52 CK52 0.9 41 1.2 73 1.9 0.73 27 1.6 70 19 99
ZK52 0.9 51 1.3 81 1.2 1 26 1.5 65 15 97
XK52 1 43 1.5 77 3.1 0.9 24 2.1 76 22 99
75 CK72 1.4 59 1.8 101 2.3 1.2 40 2 92 13 99
XK75 1.8 72 2.4 113 3.6 1.6 45 3.4 117 20 98
CX75 1.7 75 2.2 89 3.8 1.2 37 3.3 105 23
110 XK110 3.2 138 3.9 200 2.7 2 63 5.5 195 19 98
CX110 2.2 93 3.3 160 3.6 2.2 63 4.5 143 21
200 XK200 8.5 317 7.5 410 2.4 13 449 22 99

 

Our workshop:

CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite Panels 1

 

FAQ:

1. How can I get the reasonable price efficiently?

-Quantity, specification and 3D drawing will be helpful.

2. What file format are available for you to open?

-DWG, DXF, STP, IGS are available.

3. What is your payment term?

-T/T and Paypal are common, other methods could be discussed.